Effect of fluoride application on shear bond strength of brackets bonded with a resin-modified glass-ionomer

PURPOSE: The purpose of this study was to assess the effect of fluoride application at 3 different steps of the bonding process on the shear bond strength and bond failure site of a resin-modified glass ionomer cement. MATERIAL: Sixty stainless steel brackets were bonded to bovine incisors with Fuji Ortho LC (GC Europe, Leuven, Belgium) under 4 different enamel conditions: (1) uncontaminated enamel, (2) enamel precleaned with fluoride-containing prophylaxis paste, (3) 1.1% acidulated phosphate fluoride (APF) gel applied immediately before conditioning, and (4) 1.1% APF gel applied immediately before bonding. After bonding, all samples were stored in distilled water for 24 hours and subsequently tested in shear mode on a universal testing machine. RESULTS: No significant differences were found between groups 1 (uncontaminated enamel) and 2 (fluoride application during prophylaxis). Both groups showed significantly greater shear bond strength values than groups 3 (fluoride application before conditioning) and 4 (fluoride application before bonding). Groups 3 and 4 did not differ significantly. Moreover, no significant differences in debond locations were found among the 4 groups. CONCLUSIONS: Fluoride application during initial prophylaxis does not affect the bond strength values of Fuji Ortho LC, whereas it significantly lowers bond strength values when applied before both conditioning and bonding.